This pourable wear-resistant type is used in mould making
and wherever metal parts are subject to high wear caused
by friction, e.g.:
- for repairing and build-up of shafts
- for pouring out bearings, cutting and punching tools
- for making casting and profile milling models as well as drawing moulds
- for pouring under machines and foundations
- and as a wear-resistant under-coating before final coating with
WEICON Ceramic BL
WEICON Plastic Metal WR cures to a hard and wear resistant surface
with good sliding properties.
| Item number | weicon 10300020 | | GTIN | 4024596002664 |
| Item features |
|---|
| Composition | Epoxy resin steel-filled | | Specific Properties | liquid, wear resistant | | Mixing ratio by weight % (Resin/Hardener) | 100:15 | | Pot-life at +20°C (200 g preparation) | 45 Min. | | Density of the mixture | 2,3 g/cm³ | | Viscosity of the mixture | 20.000 mPa·s | | Max. layer thickness per application | 10 mm | | Cure time mechanical loads | 16 h | | final hardness | 24 h | | Mean compressive strength (+25°C) acc. to DIN 53281-83 | 110 MPa | | Mean tensile strength (+25°C) acc. to DIN 53281-83 | 33 MPa | | Mean Flexural strength (+25°C) acc. to DIN 53281-83 | 80 MPa | | Mean strength E-Modul (+25°C) acc. to DIN 53281-83 | 5.000 - 5.500 MPa | | Shore D (+25°C) acc. to DIN 53281-83 | 90 | | Shrinkage | 0,02 % | | Thermoforming resistance | 65 °C | | Colour | black | | Temperature resistance | -35 bis +120 °C |
|